耐化学PC 耐冰醋酸 四氯化氮浸泡PC塑胶原料
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| UL文件号 |
|
| 外观 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.20 | g/cm3 | ASTM D792 |
| Thickness - Layer Capability | 127.0 到 330.2 | μm |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| Volume Resistance 1 | 6.0E+13 到 2.0E+14 | ohms | ASTM D257 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 (R 级) | 115 | ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 2(3.18 mm) | 2280 | MPa | ASTM D638 |
| 抗张强度 3(3.18 mm) | 67.6 | MPa | ASTM D638 |
| 伸长率 4(断裂, 3.18 mm) | 5.0 | % | ASTM D638 |
| 弯曲模量 5 | 2230 | MPa | ASTM D790 |
| 弯曲强度 6 | 104 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 (23°C) | 53 | J/m | ASTM D256A |
| 无缺口悬臂梁冲击 (23°C) | 320 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火 | 138 | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 127 | °C | ASTM D648 |
| 玻璃转化温度 | 161 | °C | DMA |
| 维卡软化温度 | 139 | °C | ASTM D1525 |
| 线形热膨胀系数 - 流动 | 6.8E-5 | cm/cm/°C | ASTM E831 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 介电强度 | 14 到 15 | kV/mm | ASTM D149 |
| 介电常数 7 | 2.80 到 3.00 | ASTM D150 | |
| 耗散因数 8 | 5.0E-4 到 6.0E-4 | ASTM D150 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| UL 阻燃等级 | HB | UL 94 |
| 备注 | |
|---|---|
| 1 . | All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
| 2 . | 类型 1, 5.1 mm/min |
| 3 . | 类型 1, 5.1 mm/min |
| 4 . | 类型 1, 5.1 mm/min |
| 5 . | 方法 I (三点负荷), 1.3 mm/min |
| 6 . | 方法 I (三点负荷), 1.3 mm/min |
| 7 . | All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
| 8 . | All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
耐化学PC 耐冰醋酸 四氯化氮浸泡PC塑胶原料