      Category

      Trade
      mark

      Chemical composition

      主要成份(%)

      Characteristics & application

      特性和用途

      Equivalent to AWS

      相当AWS

      Hardfacing

      S 101

      C3 Cr28 Ni4
      Si3.5 Fe Rem.

      HRc48-54. Resistance to wear, gas corrosion and oxidation. Hardfacing of bucket tooth and case pump.
      HRc48-54,耐磨、耐气蚀、抗氧化。堆焊铲斗齿,泵套

       

      S 111

      C1 Cr29 W5
      Co Rem.

      HRc38-47. Resistance to wear and corrosion at high-temperature. Hardfacing of high temperature and pressure valve.
      HRc38-47,高温下耐磨、耐蚀。堆焊高温高压阀门

      ECoCr-A

      S 112

      C1.5 Cr29 W8
      Co Rem.

      HRc45-50. Resistance to wear and corrosion at high-temperature. Hardfacing of valve and hot-rolling pass.
      HRc45-50,高温下耐磨、耐蚀。堆焊阀门,热轧孔型

      ECoCr-B

      S 113

      C2.5 Cr30 W17
      Co Rem.

      HRc55. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of screw charging carriage.
      HRc55,高温下耐磨、耐热,但抗冲击性差。堆焊螺旋送料机用

       

      S 114

      C2.5 Cr30 W12
      Co Rem.

      HRc53. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of three-cone bit.
      HRc53,高温下耐磨、耐热,但抗冲击较差。堆焊牙轮钻头

      ECoCr-C

      Copper

      alloys

       

       

       

      S 201

      Sn1 Si0.3Mn0.3
      Cu Rem.

      Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper.
      机械性能好,抗裂性好。紫铜气焊及氩弧焊用

      ERCu

      S 211

      Si3 Mn1
      Cu Rem.

      Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel.
      机械性能好,铜合金氩弧焊及钢的MIG钎焊用

      ERCuSi-Al

      S 212

      Sn5 Cu Rem.

      Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
      耐磨性好。铜合金氩弧焊及钢的堆焊用

      ERCuSn-A

      S 213

      Sn8 Cu Rem.

      Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
      耐磨性好。铜合金氩弧焊及钢的堆焊用

      ERCuSn-C

      S 214

      Al7.5 Cu Rem.

      Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
      耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用

      ERCuAl-A1

      S 215

      Al9 Cu Rem.

      Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
      耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用

      ERCuAl-A2

      S 221

      Cu60 Sn1 Si0.3
      Zn Rem.

      Melting point is about 890. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
      熔点约890℃。黄铜气焊及碳弧焊用,也可钎焊铜、钢、铸铁

       

      S 221F

      Cu60 Sn1 Si 0.3
      Zn Rem.

      S221 welding rod coated with flux.
      外涂焊剂的S221焊丝

       

      S 222

      Cu58Sn0.9Si0.1
      Fe0.8 Zn Rem.

      Melting point is about 880. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
      熔点约880℃。黄铜气焊及碳弧焊用,也可钎焊铜、钢、铸铁

      RBCuZn-C

      S 222F

      Cu58Sn0.9Si0.1
      Fe0.8 Zn Rem.

      S222 welding rod coated with flux.
      外涂焊剂的S222焊丝

      RBCuZn-C

      S 223

      Cu59 Sn0.6
      Zn Rem.

      Melting point is about 900. Braze welding of copper, steel and cast iron.
      熔点约900℃。铜、钢、铸铁钎焊用

      RBCuZn-A

      S 224

      Cu62 Si0.5
      Zn Rem.

      Melting point is about 905. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
      熔点约905℃。黄铜气焊及碳弧焊用,也可钎焊铜、钢、铸铁

       

      Copper
      alloys

      S 225

      Cu48 Ni10
      Zn Rem.

      Melting point is about 935 and high strength. Braze welding of steel, nickel and carbide alloys.
      熔点约935℃。高强度,钎焊钢、镍及硬质合金用

      RBCuZn-D

      S 225F

      Cu48 Ni10
      Zn Rem.

      S225 welding rod coated with flux.
      外涂焊剂的S225焊丝

      RBCuZn-D

      S 226

      Cu60 Sn0.3
      Si0.2 Zn Rem.

      Melting point is about 900. Gas welding of brass, also braze welding of copper, steel and cast iron.
      熔点约900℃。黄铜气焊用,也可钎焊铜、钢、铸铁

       

      S 227

      Cu58Sn0.9Ni0.5
      Si0.1 Fe0.8
      Zn Rem.

      Melting point is about 880. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
      熔点880℃。黄铜气焊及碳弧焊用,也可钎焊铜、钢、铸铁

      RBCuZn-B

      S 229

      Cu55 Ni6 Mn4
      Zn

      Melting point is about 920, high strength. Braze welding of steel, nickel and hard carbide.
      熔点约920℃。高强度,钎焊钢、镍及硬质合金用

       

      Aluminum alloys

      S 301

      Al99.5

      Good ductility and corrosion resistance. Gas welding and argon arc welding of pure aluminum.
      塑性好、耐蚀。纯铝气焊、氩弧焊用

      ER1100

      S 311

      Si5 Al Rem.

      Corrosion resistance, wide range of usage. Gas welding and argon arc welding of aluminum alloys other than high magnesium alloys.
      抗裂性好,通用性大。铝合金气焊、氩弧焊用。不宜用高镁合金

      ER4043

      S 321

      Mn1.3 Al Rem.

      Good corrosion resistance, weldability and ductility. Gas welding and argon arc welding of aluminum alloys.
      良好的耐蚀性、可焊性及塑性。铝合金气焊、氩弧焊用

       

      S 331

      Mg5 Mn0.4
      Al Rem.

      Corrosion resistance and high strength. Argon arc welding of aluminum alloys.
      耐蚀,强度高。铝合金氩弧焊用

      ER5183