特 性
|
焊金耐热 耐腐蚀 耐磨耗性能优良,用于修复基体合金相似的高温加工工具,如H13钢.
硬度HRC 43～46度A hot work tool steel that is tungsten free,Good hot hardness up to 565℃.For repair of H-13 tool steels and appications in the die casting and forging industries subject to high thermal gradients.
|
|
用 途
|
焊补有色金属压铸模具 PA POM PS PE EP Weld-repair non-ferrous metal die-casting molds PA POM PS PE EP
|
|
规 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠ 2.4￠
|
|
特 性
|
Cr W V 多元合金焊丝 ，熔敷金属具有自硬性的马氏体组织。具有高硬度耐高温冲击，焊后机加工困难。硬度HRC48～52 Cr multielement alloy welding wire, w. v. deposited metal has since the rigid martensite organization. With high hardness, impact resistant machining difficulty after welding. Hardness HRC48 ~52
|
|
用 途
|
焊补热锻模 冲模 热加工工具 热切模等Hot forging die weld-repair hot-working tools etc. Eagerly
|
|
规 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠
|
|
特 性
|
焊金耐疲劳 耐热 耐磨耗冲击,一般热压铸模具常有龟裂纹状,大部分是热应力引起,热处理调至适当硬度改善其寿命,硬度太高或太低均不适用.HRC43～47 Welding gold fatigue resistance, abrasion resistance impact resistant heat die-casting molds, most often turtle crack is caused by thermal stress, heat treatment to improve its service life, suitable hardness hardness too much or too little are not applicable.
|
|
用 途
|
焊补热气冲模,铜铝锌热锻模,铝挤压模. Hot stamping, weld-repair copper aluminum and zinc hot forging, aluminum extrusion die
.
|
|
规 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠
|
|
特 性
|
放电加工,焊接性好,研磨后光滑如镜,加入易切削元素,切削加工容易,溶敷金属具有高韧性,耐磨不变形等特点,焊后只要简单热处理即可得到均一的镜面效果. 750an electro-discharge machining, welding, grinding smooth as a mirror, after joining cutting elements, machining, easy dissolve deposited metal with high toughness and wear no deformation characteristics, such as simple after welding heat can get the mirror effect uniform.
|
|
用 途
|
焊补塑胶模具NAK55 NAK80等NAK55 NAK80 weld-repair plastic mould etc
|
|
规 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠
|
|
特 性
|
马氏体时效钢,其堆焊层硬度可达HRC30～32度,溶敷金属柔软,具韧性易切削,在其500℃/2H时效处理后硬度可提高到HRC48～50度. Limitation of martensite steel, the hardfacing layer of hardness HRC30 ~ 32 degrees, soluble metal soft, apply, in its toughness cutting 500 ° c / 2H aging treatment can improve HRC48 hardness to 50 ~.
|
|
用 途
|
焊补铝压铸模具,挤压模具,冲裁模 注塑模等. Weld repairs, aluminum casting die, extrusion dies, punching mould injection mold, etc
|
|
规 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠
|
|
特 性
|
含有W Mo Cr V 的高合金焊丝,溶敷金属具有高韧性,高硬度冲击耐磨耗性能,可使用在600℃的热间环境,焊后金属可高达HRC61～63度,经热处理后硬度尚有提高. Contains W Mo Cr V high alloy welding wire, soluble deposited metal with high toughness and high hardness, impact abrasion resistance performance can be used in 600 degrees Celsius between thermal environment, after welding metal can be as high as HRC61 ~ 63 degree of hardness, still improve.
|
|
用 途
|
焊补冷热作模具,成型刀具,修整刀具 冲头 模具 粉碎机刃口,冲压模具,也可以在碳钢和低合金钢上堆焊制成新工具. Heat for mould weld-repair, molding tool, die cutter punch grinder blade, stamping, also can be in the carbon steel and the low alloy steel made on new tools. #
|
|
规 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠
|
|
特 性
|
可直接在各种铸铁/生铁材料模具上施焊,也可以做为模具龟裂之焊合,用短弧焊接较不易产生气孔及裂痕. But in all sorts of cast iron/directly on the mould material, also can make the mold cracked, with a short weld arc soldering less porosity and crack.
|
|
用 途
|
焊补铸铁,易加工雕刻. Iron, easy machining weld-repair carving.
|
|
规 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠ 2.4￠ 3.2￠
|
|
特 性
|
熔敷金属能满足较高的焊接质量和耐腐蚀性能. Deposited metal can meet high welding quality and corrosion resistance.
|
|
用 途
|
用于铸铁 碳钢 不锈钢和低合金钢的焊接. For carbon steel and low alloy steel iron welding.
|
|
规 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠ 2.4￠ 3.2￠
|
|
特 性
|
含镍铬成份高,拉力强 硬度HB-300. Containing nickel chrome component high hardness, tensile strong HB - 300
.
|
|
用 途
|
异材焊接 硬面制作打底,高强度钢接合 龟裂焊补. Different welding materials production, hardfaced with high strength steel render junction weld-repair cracked
|
|
规 格
|
0.9￠ 1.2￠ 1.6￠ 2.0￠
|
|
特 性
|
氩弧焊铜 优异的机械加工性能 硬度HB-200. Argon arc welding copper excellent machining performance hardness HB - 200.
|
|
用 途
|
广泛用于电解片 铜合金 钢 青铜 生铁铜件之焊补. Widely used in electrolytic copper alloy steel cast bronze pieces of copper pieces of weld-repair.
|
|
规 格
|
0.9￠ 1.2￠ 1.6￠ 2.0￠
|
|
特 性
|
马氏体不锈钢,耐腐蚀,抛光性能优异,热处理性能稳定 硬度HRC51~53. Martensitic stainless steel corrosion resistance, excellent polishing treatment stable performance HRC51 hardness - 53.
|
|
用 途
|
适用于420不锈钢的焊接. Applicable to 420 stainless steel welding.
|
|
规 格
|
0.9￠ 1.2￠ 1.6￠ 2.0￠
|
|
特 性
|
焊金耐热 耐腐蚀 耐磨耗性能优良,用于修复基体合金相似的高温加工工具,如H13钢.
硬度HRC 43～46度A hot work tool steel that is tungsten free,Good hot hardness up to 565℃.For repair of H-13 tool steels and appications in the die casting and forging industries subject to high thermal gradients.
|
|
用 途
|
焊补有色金属压铸模具 PA POM PS PE EP Weld-repair non-ferrous metal die-casting molds PA POM PS PE EP
|
|
规 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠ 2.4￠
|
|
特 性
|
Cr W V 多元合金焊丝 ，熔敷金属具有自硬性的马氏体组织。具有高硬度耐高温冲击，焊后机加工困难。硬度HRC48～52 Cr multielement alloy welding wire, w. v. deposited metal has since the rigid martensite organization. With high hardness, impact resistant machining difficulty after welding. Hardness HRC48 ~52
|
|
用 途
|
焊补热锻模 冲模 热加工工具 热切模等Hot forging die weld-repair hot-working tools etc. Eagerly
|
|
规 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠
|
|
特 性
|
焊金耐疲劳 耐热 耐磨耗冲击,一般热压铸模具常有龟裂纹状,大部分是热应力引起,热处理调至适当硬度改善其寿命,硬度太高或太低均不适用.HRC43～47 Welding gold fatigue resistance, abrasion resistance impact resistant heat die-casting molds, most often turtle crack is caused by thermal stress, heat treatment to improve its service life, suitable hardness hardness too much or too little are not applicable.
|
|
用 途
|
焊补热气冲模,铜铝锌热锻模,铝挤压模. Hot stamping, weld-repair copper aluminum and zinc hot forging, aluminum extrusion die
.
|
|
规 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠
|
|
特 性
|
放电加工,焊接性好,研磨后光滑如镜,加入易切削元素,切削加工容易,溶敷金属具有高韧性,耐磨不变形等特点,焊后只要简单热处理即可得到均一的镜面效果. 750an electro-discharge machining, welding, grinding smooth as a mirror, after joining cutting elements, machining, easy dissolve deposited metal with high toughness and wear no deformation characteristics, such as simple after welding heat can get the mirror effect uniform.
|
|
用 途
|
焊补塑胶模具NAK55 NAK80等NAK55 NAK80 weld-repair plastic mould etc
|
|
规 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠
|
|
特 性
|
马氏体时效钢,其堆焊层硬度可达HRC30～32度,溶敷金属柔软,具韧性易切削,在其500℃/2H时效处理后硬度可提高到HRC48～50度. Limitation of martensite steel, the hardfacing layer of hardness HRC30 ~ 32 degrees, soluble metal soft, apply, in its toughness cutting 500 ° c / 2H aging treatment can improve HRC48 hardness to 50 ~.
|
|
用 途
|
焊补铝压铸模具,挤压模具,冲裁模 注塑模等. Weld repairs, aluminum casting die, extrusion dies, punching mould injection mold, etc
|
|
规 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠
|
|
特 性
|
含有W Mo Cr V 的高合金焊丝,溶敷金属具有高韧性,高硬度冲击耐磨耗性能,可使用在600℃的热间环境,焊后金属可高达HRC61～63度,经热处理后硬度尚有提高. Contains W Mo Cr V high alloy welding wire, soluble deposited metal with high toughness and high hardness, impact abrasion resistance performance can be used in 600 degrees Celsius between thermal environment, after welding metal can be as high as HRC61 ~ 63 degree of hardness, still improve.
|
|
用 途
|
焊补冷热作模具,成型刀具,修整刀具 冲头 模具 粉碎机刃口,冲压模具,也可以在碳钢和低合金钢上堆焊制成新工具. Heat for mould weld-repair, molding tool, die cutter punch grinder blade, stamping, also can be in the carbon steel and the low alloy steel made on new tools. #
|
|
规 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠
|
|
特 性
|
可直接在各种铸铁/生铁材料模具上施焊,也可以做为模具龟裂之焊合,用短弧焊接较不易产生气孔及裂痕. But in all sorts of cast iron/directly on the mould material, also can make the mold cracked, with a short weld arc soldering less porosity and crack.
|
|
用 途
|
焊补铸铁,易加工雕刻. Iron, easy machining weld-repair carving.
|
|
规 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠ 2.4￠ 3.2￠
|
|
特 性
|
熔敷金属能满足较高的焊接质量和耐腐蚀性能. Deposited metal can meet high welding quality and corrosion resistance.
|
|
用 途
|
用于铸铁 碳钢 不锈钢和低合金钢的焊接. For carbon steel and low alloy steel iron welding.
|
|
规 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠ 2.4￠ 3.2￠
|
|
特 性
|
含镍铬成份高,拉力强 硬度HB-300. Containing nickel chrome component high hardness, tensile strong HB - 300
.
|
|
用 途
|
异材焊接 硬面制作打底,高强度钢接合 龟裂焊补. Different welding materials production, hardfaced with high strength steel render junction weld-repair cracked
|
|
规 格
|
0.9￠ 1.2￠ 1.6￠ 2.0￠
|
|
特 性
|
氩弧焊铜 优异的机械加工性能 硬度HB-200. Argon arc welding copper excellent machining performance hardness HB - 200.
|
|
用 途
|
广泛用于电解片 铜合金 钢 青铜 生铁铜件之焊补. Widely used in electrolytic copper alloy steel cast bronze pieces of copper pieces of weld-repair.
|
|
规 格
|
0.9￠ 1.2￠ 1.6￠ 2.0￠
|
|
特 性
|
马氏体不锈钢,耐腐蚀,抛光性能优异,热处理性能稳定 硬度HRC51~53. Martensitic stainless steel corrosion resistance, excellent polishing treatment stable performance HRC51 hardness - 53.
|
|
用 途
|
适用于420不锈钢的焊接. Applicable to 420 stainless steel welding.
|
|
规 格
|
0.9￠ 1.2￠ 1.6￠ 2.0￠
|