CLASSIFICATION

EN 14700 T Fe10

DESCRIPTION

• Tubular wire for submerged arc hardfacing
• Austenitic stainless weld deposit
• Good impact, cavitation and corrosion resistance
• The weld deposit work hardens to different degrees depending on amount of impact
• Resists scaling up to 850°C, good resistance to thermal shocks

APPLICATIONS

• Hardface 19 9 6-G is mainly used to rebuild components exposed to high impact and corrosion.
• Sub-layer before hardfacing

Examples
Steel mill rolls, metallurgical plant guides, tram and train rails and fittings, high speed forming rolls

TYPICAL ALL-WELD METAL ANALYSIS CMnSiCrNi

0.10	6.00	0.50	19.0	9.0

Structure: austenite

TYPICAL ALL-WELD METAL MECHANICAL PROPERTIES Hardness – 3-Layer deposit: As welded 180 HBWork hardened: 47 HRc CONDITIONS OF USE Current typeShielding

DC (+)	WAF 325 or WAF 385

FLUX DESCRIPTIONWAF 325WAF 385

Classification	EN 760: S A FB 1 65 DC H5	EN 760: S A AB 2 65 DC H5
Redrying	2 hours at 250 - 350°C
Packaging	bags (25 kg)

OPERATING CONDITIONS DiameterAmperage [A]Voltage [V]Stick-out [mm] [mm]RangeOptimumRangeOptimumRangeOptimum

1.6	150 - 300	250	26 - 32	30	15 - 30	25
2.0	200 - 350	270	26 - 32	30	20 - 50	25
2.4	200 - 450	350	26 - 32	30	25 - 50	30
2.8	250 - 550	400	28 - 32	30	25 - 50	30
3.2	300 - 650	500	28 - 32	30	25 - 50	30

Recovery: 95 %

WELDING POSITIONS

Flat

STANDARD DIAMETERS (mm)

1.6, 2.0, 2.4, 2.8, 3.2
Other diameters: please consult us

PACKAGING Diameter≤ 2.4 mm≥ 2.4 mm

Standard packaging [EN ISO 544]	Spool : BS 300	Coil : B 450	Drum
Weight	15 kg	25 kg	Up to 330 kg

Other packaging: please consult us