黑龙江L302斯米克Ag25Cu40银焊条经销商L302 Wire & rod 丝 745-775 Ag25 Cu40 Zn Rem. Brazing of copper, copper alloys, steel and stainless steel etc. 钎焊铜及铜合金、钢及不锈钢等

Category 类 别	Trade- Mark 牌 号	Equivalent to China Standard 相当国标	Characteristics & application 特性和用途	Equivalent to AWS 相当AWS
Hard-surfacing 硬 面 堆 焊	D 667	EDZCr-B-15	HRc≥48. Resistance to wear, gas corrosion and oxidation. Hardfacing of blast furnace hopper and cracker part. HRc≥48，耐磨、耐气蚀、抗氧化。堆焊高炉料钟、破碎机件
	D 802	EDCoCr-A-03	HRc38-47. Resistance to heat, wear and corrosion. Hardfacing of high temperature part such as the edge of thermo-cutter. HRc38-47，耐热、耐蚀、耐磨。堆焊高温工件如热剪切刀刃	ECoCr-A
	D 812	EDCoCr-B-03	HRc45-50. Resistance to heat, wear and corrosion. Hardfacing of high temperature part such as internal-combustion engine valve. HRc45-50，耐热、耐蚀、耐磨。堆焊高温工件如内燃机阀	ECoCr-B
	D 822		HRc≥53. Resistance to Wear and heat, bad shock resistance. Hardfacing of rotating blade wheel of boiler. HRc≥53，耐热、耐磨，但抗冲击性差。堆焊锅炉旋转叶轮
	D 832	EDCoCr-C-03	HRc≥50. Wear and heat resistance. Hardfacing of high temperature part such as hot-rolling guided way. HRc≥50，耐热、耐磨。堆焊高温工件如热轧导轨	ECoCr-C
	D 842	EDCoCr-D-03	HRc28-38. Corrosion and thermo-fatigue resistance, work harding. Hardfacing of hot forging die. HRc28-38，耐蚀、抗热疲劳，具有加工硬化性。堆焊热锻模
Cast iron 铸 铁	Z 308	EZNi	Pure nickel, excellent general properties. Used to weld thin cast iron part and repair welding machined surface, such as guided way of machine tool. 纯镍，综合性能好。铸铁薄件及加工面补焊用，如机床导卫	ENi-Cl
	Z 408	EZNiFe	Iron nickel, high strength and excellent ductility. Repair welding of important gray cast iron and nodular cast iron, such as cylinder cap. 镍铁，强度高、塑性好。重要灰铸铁及球铁焊补用，如汽缸盖	ENiFe-Cl
	Z 508	EZNiCu-1	Copper nickel, good machinability and bad crack resistance. Repair welding of sand hole and gray cast iron machined surface subject to no load. 镍铜，易加工，但抗裂性较差。不受力的灰铸铁加工面及砂眼补焊	ENiCu-B
Copper alloys 铜 合 金	Cu 107	ECu	Red copper, atmosphere and sea water corrosion and excellent electric conductivity. Welding of red copper such as electrical copper row. 紫铜，耐大气，海水腐蚀，导电性好。紫铜焊接用，如导电铜排	ECu
	Cu 207	ECuSi	Silicon bronze, corrosion resistance and high strength. Welding of copper, silicon bronze and brass. 硅青铜，耐蚀、强度高。铜、硅青铜及黄铜焊接用	ECuSi
	Cu 227	ECuSnB	Tin phosphor bronze, corrosion resistance and high strength. Welding of copper, silicon bronze and brass. 锡磷青铜，耐蚀、强度高。铜、硅青铜及黄铜焊接用	ECuSn-C
	Cu 237	ECuAl	Aluminum bronze, wear and corrosion and high strength. Welding or surfacing of copper alloys. 铝青铜，耐磨、耐蚀，强度高。铜合金焊接或堆焊用	ECuAl-A2
Aluminum alloys 铝 合 金	Al 109	TAl	Pure aluminum, excellent corrosion resistance and middle strength. Welding of pure aluminum. 纯铝，耐蚀性好，但强度不高，纯铝焊接用	E1100
	Al 209	TAlSi	Silicon aluminum, good crack resistance and wide range of usage. Welding of aluminum alloys other than aluminum magnesium alloys. 铝硅，抗裂性好，通用性大。铝合金焊接用，不宜焊接铝镁合金	E4043
	Al 309	TAMn	Manganese aluminum, corrosion resistance and high strength. Welding of aluminum alloys. 铝锰，强度高，耐蚀。铝合金焊接用	E3003
Nickel alloys 镍合金	Ni 102	ENi-1	Pure nickel. Welding and surfacing of nickel and nickel to steel. 纯镍，用于镍、镍与钢的焊接与堆焊	ENi-1
	Ni 207	ENiCu-7	Copper nickel. Welding and surfacing of copper nickel and copper nickel to steel. 镍铜，用于镍铜、镍铜与钢的焊接与堆焊	ENiCu-7

Category 类 别	Trade mark 牌 号	Chemical composition 主要成份(%)	Characteristics & application 特性和用途	Equivalent to AWS 相当AWS
Hardfacing 硬 面 堆 焊	S 101	C3 Cr28 Ni4 Si3.5 Fe Rem.	HRc48-54. Resistance to wear, gas corrosion and oxidation. Hardfacing of bucket tooth and case pump. HRc48-54，耐磨、耐气蚀、抗氧化。堆焊铲斗齿，泵套
	S 111	C1 Cr29 W5 Co Rem.	HRc38-47. Resistance to wear and corrosion at high-temperature. Hardfacing of high temperature and pressure valve. HRc38-47，高温下耐磨、耐蚀。堆焊高温高压阀门	ECoCr-A
	S 112	C1.5 Cr29 W8 Co Rem.	HRc45-50. Resistance to wear and corrosion at high-temperature. Hardfacing of valve and hot-rolling pass. HRc45-50，高温下耐磨、耐蚀。堆焊阀门，热轧孔型	ECoCr-B
	S 113	C2.5 Cr30 W17 Co Rem.	HRc≥55. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of screw charging carriage. HRc≥55，高温下耐磨、耐热，但抗冲击性差。堆焊螺旋送料机用
	S 114	C2.5 Cr30 W12 Co Rem.	HRc≥53. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of three-cone bit. HRc≥53，高温下耐磨、耐热，但抗冲击较差。堆焊牙轮钻头	ECoCr-C
Copper alloys   铜 　 合 　 金	S 201	Sn1 Si0.3Mn0.3 Cu Rem.	Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper. 机械性能好，抗裂性好。紫铜气焊及氩弧焊用	ERCu
	S 211	Si3 Mn1 Cu Rem.	Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel. 机械性能好，铜合金氩弧焊及钢的MIG钎焊用	ERCuSi-Al
	S 212	Sn5 Cu Rem.	Wear resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨性好。铜合金氩弧焊及钢的堆焊用	ERCuSn-A
	S 213	Sn8 Cu Rem.	Wear resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨性好。铜合金氩弧焊及钢的堆焊用	ERCuSn-C
	S 214	Al7.5 Cu Rem.	Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用	ERCuAl-A1
	S 215	Al9 Cu Rem.	Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用	ERCuAl-A2
	S 221	Cu60 Sn1 Si0.3 Zn Rem.	Melting point is about 890℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔点约890℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁
	S 221F	Cu60 Sn1 Si 0.3 Zn Rem.	S221 welding rod coated with flux. 外涂焊剂的S221焊丝
	S 222	Cu58Sn0.9Si0.1 Fe0.8 Zn Rem.	Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔点约880℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁	RBCuZn-C
	S 222F	Cu58Sn0.9Si0.1 Fe0.8 Zn Rem.	S222 welding rod coated with flux. 外涂焊剂的S222焊丝	RBCuZn-C
	S 223	Cu59 Sn0.6 Zn Rem.	Melting point is about 900℃. Braze welding of copper, steel and cast iron. 熔点约900℃。铜、钢、铸铁钎焊用	RBCuZn-A
	S 224	Cu62 Si0.5 Zn Rem.	Melting point is about 905℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔点约905℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁
Copper alloys 铜 合 金	S 225	Cu48 Ni10 Zn Rem.	Melting point is about 935℃ and high strength. Braze welding of steel, nickel and carbide alloys. 熔点约935℃。高强度,钎焊钢、镍及硬质合金用	RBCuZn-D
	S 225F	Cu48 Ni10 Zn Rem.	S225 welding rod coated with flux. 外涂焊剂的S225焊丝	RBCuZn-D
	S 226	Cu60 Sn0.3 Si0.2 Zn Rem.	Melting point is about 900℃. Gas welding of brass, also braze welding of copper, steel and cast iron. 熔点约900℃。黄铜气焊用，也可钎焊铜、钢、铸铁
	S 227	Cu58Sn0.9Ni0.5 Si0.1 Fe0.8 Zn Rem.	Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔点880℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁	RBCuZn-B
	S 229	Cu55 Ni6 Mn4 Zn余	Melting point is about 920℃, high strength. Braze welding of steel, nickel and hard carbide. 熔点约920℃。高强度,钎焊钢、镍及硬质合金用
Aluminum alloys 铝 合 金	S 301	Al≥99.5	Good ductility and corrosion resistance. Gas welding and argon arc welding of pure aluminum. 塑性好、耐蚀。纯铝气焊、氩弧焊用	ER1100
	S 311	Si5 Al Rem.	Corrosion resistance, wide range of usage. Gas welding and argon arc welding of aluminum alloys other than high magnesium alloys. 抗裂性好，通用性大。铝合金气焊、氩弧焊用。不宜用高镁合金	ER4043
	S 321	Mn1.3 Al Rem.	Good corrosion resistance, weldability and ductility. Gas welding and argon arc welding of aluminum alloys. 良好的耐蚀性、可焊性及塑性。铝合金气焊、氩弧焊用
	S 331	Mg5 Mn0.4 Al Rem.	Corrosion resistance and high strength. Argon arc welding of aluminum alloys. 耐蚀，强度高。铝合金氩弧焊用	ER5183