GTX910耐化学尺寸稳定PPO

NORYL GTX Resin GTX910

PPO 基础创新塑料（美国）GTX910

PPE+PS+尼龙，汽车零部件组件。尺寸稳定性。优秀的耐化学性。表面外观光洁。

物性表：

TYPICAL PROPERTIES ⁽¹⁾
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	59	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	55	MPa	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	60	%	ASTM D 638
Flexural Stress, yld, 2.6 mm/min, 100 mm span	95	MPa	ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span	2240	MPa	ASTM D 790
Hardness, Rockwell R	116	-	ASTM D 785
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	240	J/m	ASTM D 256
Izod Impact, notched, -30°C	133	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	50	J	ASTM D 3763
Instrumented Impact Energy @ peak, -30	39	J	ASTM D 3763
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	232	°C	ASTM D 1525
HDT, 0.45 MPa, 6.4 mm, unannealed	193	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	143	°C	ASTM D 648
CTE, -40°C to 95°C, flow	9.E-05	1/°C	ASTM E 831
CTE, -40°C to 95°C, xflow	9.E-05	1/°C	ASTM E 831
CTE, 60°C to 138°C, flow	1.26E-04	1/°C	ASTM E 831
CTE, 60°C to 138°C, xflow	1.26E-04	1/°C	ASTM E 831
Relative Temp Index, Elec	50	°C	UL 746B
Relative Temp Index, Mech w/impact	50	°C	UL 746B
Relative Temp Index, Mech w/o impact	50	°C	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.1	-	ASTM D 792
Density	1.107	g/cm3	ASTM D 792
Water Absorption, 50% RH, equilib	1	%	ASTM D 570
Moisture Absorption, 50% RH, 24 hrs	0.5	%	ASTM D 570
Mold Shrinkage, flow, 3.2 mm (5)	1.1 - 1.3	%	SABIC Method
Mold Shrink, flow, annealed 130C 1hr (5)	1.6 - 1.8	%	ASTM D 955
Mold Shrinkage, xflow, 3.2 mm (5)	1 - 1.2	%	SABIC Method
ELECTRICAL	Value	Unit	Standard
Arc Resistance, Tungsten {PLC}	7	PLC Code	ASTM D 495
Hot Wire Ignition {PLC)	3	PLC Code	UL 746A
High Voltage Arc Track Rate {PLC}	4	PLC Code	UL 746A
High Ampere Arc Ign, surface {PLC}	0	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	1	PLC Code	UL 746A
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94HB Flame Class Rating (3)	1.49	mm	UL 94