NORYL HS2000X PPO无溴阻燃V0/5VA

NORYL Resin HS2000X

PPO 基础创新塑料(美国) HS2000X-701

性能特点：矿物填料17%增强,无溴阻燃,尺寸稳定.PPE+PS

PPE + PS混合。17%的矿物增强。Non-brominated non-chlorinated FR系统。阻燃UL94 V0 / 5VA 等级。UL746C f1。绝缘强度。尺寸稳定性。适合市场E / E室内/室外的应用包括电气天花板盒和烟雾探测器。

物性数据：

溶指7.6，收缩率0.5-0.7%，冲击强度130J/M，热变形温度108-128℃，维卡软化温度132-136℃，表面电阻率>1.0E+16ohm，体积电阻率1.2E+16ohm.cm，加工熔体温度282-310℃。

TYPICAL PROPERTIES ⁽¹⁾
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	750	kgf/cm2	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	610	kgf/cm2	ASTM D 638
Tensile Strain, yield	3.8	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	8.4	%	ASTM D 638
Tensile Modulus, 5 mm/min	37200	kgf/cm2	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	1190	kgf/cm2	ASTM D 790
Flexural Stress, yld, 2.6 mm/min, 100 mm span	1190	kgf/cm2	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	37400	kgf/cm2	ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span	36200	kgf/cm2	ASTM D 790
Tensile Stress, yield	71	MPa	ISO 527
Tensile Stress, break	57	MPa	ISO 527
Tensile Strain, yield	3.7	%	ISO 527
Tensile Strain, break	10.5	%	ISO 527
Tensile Modulus, 1 mm/min	4000	MPa	ISO 527
Flexural Stress	117	MPa	ISO 178
Flexural Modulus	3800	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	227	cm-kgf/cm	ASTM D 4812
Izod Impact, notched, 23°C	13	cm-kgf/cm	ASTM D 256
Izod Impact, Reverse Notched, 3.2 mm	82	cm-kgf/cm	ASTM D 256
Instrumented Impact Total Energy, 23°C	4517	cm-kgf	ASTM D 3763
Izod Impact, notched 80104 +23°C	9	kJ/m2	ISO 180/1A
Charpy Impact, notched, 23°C	10	kJ/m2	ISO 179/2C
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	117	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	108	°C	ASTM D 648
HDT, 0.45 MPa, 6.4 mm, unannealed	128	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	116	°C	ASTM D 648
CTE, -40°C to 40°C, flow	7.06E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	7.76E-05	1/°C	ASTM E 831
Vicat Softening Temp, Rate B/50	132	°C	ISO 306
Vicat Softening Temp, Rate B/120	136	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm	126	°C	ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm	111	°C	ISO 75/Ae
Relative Temp Index, Elec	100	°C	UL 746B
Relative Temp Index, Mech w/impact	85	°C	UL 746B
Relative Temp Index, Mech w/o impact	100	°C	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.25	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)	0.5 - 0.7	%	SABIC Method
Melt Flow Rate, 280°C/5.0 kgf	7.6	g/10 min	ASTM D 1238
Melt Flow Rate, 300°C/5.0 kgf	7.6	g/10 min	ASTM D 1238
Melt Volume Rate, MVR at 280°C/5.0 kg	6	cm3/10 min	ISO 1133
Melt Volume Rate, MVR at 300°C/5.0 kg	6	cm3/10 min	ISO 1133
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	1.2E+16	Ohm-cm	ASTM D 257
Surface Resistivity	>1.E+16	Ohm	ASTM D 257
Dielectric Strength, in oil, 3.2 mm	17.3	kV/mm	ASTM D 149
Relative Permittivity, 50/60 Hz	2.89	-	ASTM D 150
Relative Permittivity, 1 MHz	2.7	-	ASTM D 150
Dissipation Factor, 50/60 Hz	0.017	-	ASTM D 150
Dissipation Factor, 1 MHz	0.0044	-	ASTM D 150
Arc Resistance, Tungsten {PLC}	6	PLC Code	ASTM D 495
Hot Wire Ignition {PLC)	0	PLC Code	UL 746A
High Voltage Arc Track Rate {PLC}	3	PLC Code	UL 746A
High Ampere Arc Ign, surface {PLC}	2	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	2	PLC Code	UL 746A
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94V-0 Flame Class Rating (3)	1.47	mm	UL 94
UL Recognized, 94-5VA Rating (3)	2	mm	UL 94
Radiant Panel Listing	YES	-	UL Tested
UV-light, water exposure/immersion	F1	-	UL 746C