NORYL Resin GFN3

PPO 基础创新塑料(美国) GFN3-111

玻纤30%增强

特点：PPE+PS，NSF61，尺寸稳定性好,水解稳定,工程应用。PPE + PS混合。30%的玻璃纤维。NSF61。FDA合规(限制)。低吸水率。水解稳定性。尺寸稳定性。

用途：泵件，滤材。适用于流体工程应用包括泵外壳、泵叶轮和水表组件。

物性：溶指8.7，收缩率0.1-0.4%，吸水率0.06%，洛氏硬度计108L，冲击强度120J/M，热变形温度137-158℃，维卡软化温度143-147℃，加工熔体温度299-327℃。

TYPICAL PROPERTIES ⁽¹⁾
MECHANICAL	Value	Unit	Standard
Tensile Stress, brk, Type I, 5 mm/min	1180	kgf/cm2	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	2	%	ASTM D 638
Tensile Modulus, 5 mm/min	93300	kgf/cm2	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	1830	kgf/cm2	ASTM D 790
Flexural Stress, yld, 2.6 mm/min, 100 mm span	1650	kgf/cm2	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	81500	kgf/cm2	ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span	73100	kgf/cm2	ASTM D 790
Hardness, Rockwell L	108	-	ASTM D 785
Tensile Stress, break	117	MPa	ISO 527
Tensile Strain, break	1.8	%	ISO 527
Tensile Modulus, 1 mm/min	8740	MPa	ISO 527
Flexural Stress	183	MPa	ISO 178
Flexural Modulus	8710	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	59	cm-kgf/cm	ASTM D 4812
Izod Impact, notched, 23°C	11	cm-kgf/cm	ASTM D 256
Izod Impact, notched, -30°C	12	cm-kgf/cm	ASTM D 256
Izod Impact, unnotched 80104 +23°C	31	kJ/m2	ISO 180/1U
Izod Impact, unnotched 80104 -30°C	35	kJ/m2	ISO 180/1U
Izod Impact, notched 80104 +23°C	12	kJ/m2	ISO 180/1A
Izod Impact, notched 80104 -30°C	11	kJ/m2	ISO 180/1A
Charpy Impact, notched, 23°C	12	kJ/m2	ISO 179/2C
Charpy Impact, notched, -30°C	11	kJ/m2	ISO 179/2C
Charpy 23°C, Unnotch Edgew 80104 sp=62mm	39	kJ/m2	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80104 sp=62mm	47	kJ/m2	ISO 179/1eU
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	142	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	137	°C	ASTM D 648
HDT, 0.45 MPa, 6.4 mm, unannealed	158	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	137	°C	ASTM D 648
CTE, -40°C to 40°C, flow	3.06E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	6.18E-05	1/°C	ASTM E 831
Vicat Softening Temp, Rate B/50	143	°C	ISO 306
Vicat Softening Temp, Rate B/120	147	°C	ISO 306
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	143	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	137	°C	ISO 75/Af
Relative Temp Index, Elec	90	°C	UL 746B
Relative Temp Index, Mech w/impact	90	°C	UL 746B
Relative Temp Index, Mech w/o impact	90	°C	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.29	-	ASTM D 792
Water Absorption, 24 hours	0.06	%	ASTM D 570
Mold Shrinkage, flow, 3.2 mm (5)	0.1 - 0.4	%	SABIC Method
Melt Flow Rate, 300°C/5.0 kgf	8.6	g/10 min	ASTM D 1238
Melt Volume Rate, MVR at 300°C/5.0 kg	7	cm3/10 min	ISO 1133
ELECTRICAL	Value	Unit	Standard
Dielectric Strength, in oil, 3.2 mm	21.6	kV/mm	ASTM D 149
Relative Permittivity, 50/60 Hz	2.93	-	ASTM D 150
Dissipation Factor, 50/60 Hz	0.0009	-	ASTM D 150
Arc Resistance, Tungsten {PLC}	7	PLC Code	ASTM D 495
Hot Wire Ignition {PLC)	4	PLC Code	UL 746A
High Voltage Arc Track Rate {PLC}	3	PLC Code	UL 746A
High Ampere Arc Ign, surface {PLC}	4	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	4	PLC Code	UL 746A
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94HB Flame Class Rating (3)	1.47	mm	UL 94
Oxygen Index (LOI)	26	%	ASTM D 2863