超细镍基合金粉 镍基合金粉末Ni60 Ni60A Ni60B

 

牌号

硬度

化学成分（%）

Ni15A

15

C 0.1, Si2, B1.2，Cr0.5, Fe≤5,   Ba1 Ni

Ni17A

17

C 0.1, Si2, B1,   Cr1,   Fe≤5,   Ba1  Ni

Ni20A

20

C 0.1, Si3, B1,   Cr1,   Fe≤6,   Ba1  Ni

Ni20B

20

C 0.1, Si3, B1,   Cr5,   Fe≤15,  Ba1  Ni

Ni22A

22

C 0.1, Si3, B1,   Cr1,   Fe≤0.1, Ba1  Ni

Ni25A

25

C 0.1, Si3, B1,   Cr1,   Fe≤6,   Ba1  Ni

Ni25B

25

C 0.3, Si3, B1,   Cr5,   Fe≤15,  Ba1  Ni

Ni35A

35

C 0.3, Si3, B2.2，Cr10,  Fe≤5,   Ba1  Ni

Ni35B

35

C 0.3, Si3, B2.2，Cr10,  Fe≤15,  Ba1  Ni

Ni40A

40

C 0.3, Si3, B2.5，Cr12,  Fe≤5,   Ba1  Ni

Ni45A

45

C 0.4, Si3, B2.8，Cr12,  Fe≤5,   Ba1   Ni

Ni45B

45

C 0.4, Si3, B2.8，Cr12,  Fe≤15,  Ba1  Ni

Ni50A

50

C 0.5, Si3, B3，  Cr12,  Fe≤5,   Ba1  Ni

Ni50B

50

C 0.5, Si3, B3，  Cr12,  Fe≤15,  Ba1  Ni

Ni55A

55

C 0.8, Si4, B3，  Cr14,  Fe≤5,   Ba1  Ni

Ni55B

55

C 0.8, Si4, B3，  Cr14,  Fe≤15,  Ba1  Ni

Ni60AA

60

C 0.9, Si4, B3.2，Cr16,  Fe≤2.4, Ba1  Ni

Ni60A

60

C 0.9, Si4, B3.2，Cr16,  Fe≤5,   Ba1   Ni

Ni60B

60

C 0.9, Si4, B3.2，Cr16,  Fe≤15,  Ba1   Ni

Ni60CuMo

60

C 0.9, Si4, B4,   Cr16,  Fe≤5,   Cu3.2  Mo3,   Ba1  Ni

Ni60CuMoW

60

C 0.9, Si4, B3.2, Cr16,  Fe≤5,  Cu3.2   Mo3, W3,  Ba1 Ni

Ni65

65

C 1.1,Si4,  B4，Cr18,    Fe≤15,  Ba1  Ni

Ni25C

25

C≤0.2，Si2-3.5,B1-2,Cr5-10,Fe≤4，O≤0.05   Bal Ni

Ni35C

35

C≤0.4，Si2-3.5,B1.5-2.5,Cr7-10,Fe≤4，O≤0.05  Bal Ni

Ni45C

45

C≤0.3-0.6，Si2-3.5,B2-3,Cr11-15,Fe≤5，O≤0.05  Bal Ni

Ni55C

55

C≤0.5-0.9，Si3.5-5,B2.5-4,Cr14-17,Fe≤5，O≤0.05  Bal Ni

Ni60C

60

C≤0.5-1.1，Si3-5,B3-4,Cr15-20,Fe≤5，O≤0.05   Bal Ni

 

 

简介：镍基自熔合金粉末以良好的润湿性、耐蚀性、高温自润性和合适的价格在激光熔覆材料中应用最广。主要适用于

局部要求耐磨、耐热腐蚀及抗热疲劳的构件，所需激光功率密度比铁基略高。运用Fe、Cr、Co、Mo、W等元素进行奥氏体

固溶强化。对于碳钢、不锈钢、合金钢、、铸钢等基材有较好的适应性。含硫钢基材慎用

粒度：-100  -200  -325  -400目