ENiCrMo-10 offers good pitting and crevice corrosion resistance and is an outstanding |
||||||
| dissimilar welding alloy. This wire welds nickel-chromium-molybdenum to itself,to steel,to | ||||||
| other nickel base alloy and for cladding steel with NICRMO weld metal. |
| CLASSIFICATIONS: | ||||||
| ENiCrMo-10 | ||||||
| AWS A5.11 | ||||||
| ASME SFA 5.11 | ||||||
| UNS W86022 | ||||||
| APPLICATIONS: | ||||||
| ENiCrMo-10 is formulat-ed for welding a wide array of industrial applications including power | ||||||
| generations, petroleum and chemical plants as well as offshore and marine facilities. | ||||||
| DIAMETERS: | ||||||
| 3/32'',1/8'', | ||||||
| 5/32'',3/16'' | ||||||
| TYPICAL | ||||||
| MECHANICAL PROPERTIES: | ||||||
| Tensile Strength (psi) 100,000 | ||||||
| Percent Elongation 25 | ||||||
| TYPICAL | ||||||
| CHEMICAL COMPOSITION: | ||||||
| C | Mn | P | S | Si | Ni | |
| 0.01 | 0.20 | 0.01 | <0.001 | 0.20 | Remain | |
| Cr | Mo | V | Cu | Fe | Co | |
| 21.00 | 14.00 | <0.008 | 0.07 | 2.60 | 0.18 | |
| W | ||||||
| 3.10 | ||||||
|
ENiCrMo-13 provides superb corrosion resistance and high mechanical strength, which is |
||||||
| featuring outstanding weldability and very low sensitivity to hot cracking. This electrode is a | ||||||
| nickel-chromium-molybdenum alloy with extra low carbon and silicon contents. Due to its |
| chemical composition, ENiCrMo-13 is resistant to attack by chloride ions in low PH media. | ||||||
| CLASSIFICATIONS: | ||||||
| ENiCrMo-13 | ||||||
| AWS A5.11 | ||||||
| ASME SFA 5.11 | ||||||
| UNS W86059 | ||||||
| APPLICATIONS: | ||||||
| ENiCrMo-13 is not prone to grain-boundary precipitation during hot forming and welding . | ||||||
| It is, therefore,a good choice for welding in the corrosive environment of chemical processing | ||||||
| plants. | ||||||
| DIAMETERS: | ||||||
| 3/32'',1/8'', | ||||||
| 5/32'',3/16'' | ||||||
| TYPICAL | ||||||
| MECHANICAL PROPERTIES: | ||||||
| Tensile Strength (psi) 110,000 | ||||||
| Percent Elongation 25 | ||||||
| TYPICAL | ||||||
| CHEMICAL COMPOSITION: | ||||||
| C | Mn | P | S | Si | Ni | |
| 0.005 | 0.34 | 0.013 | 0.002 | 0.10 | 59.70 | |
| Cr | Mo | Al | Fe | Co | ||
| 22.90 | 15.10 | <0.30 | 1.10 | 0.04 | ||