②原料技术数据
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
黑色 |
ASTM D-792 |
1.62 |
--- |
| 泰伯摩擦 |
--- |
ASTM D-1044 |
63 |
mg |
| 模缩率 |
流向1.6mm |
ASTM D-955 |
-0.1 |
% |
| 模缩率 |
流向3.2mm |
ASTM D-955 |
0 |
% |
| 模缩率 |
横向1.6mm |
ASTM D-955 |
0.9 |
% |
| 机械性能 |
模缩率 |
横向3.2mm |
ASTM D-955 |
0.8 |
% |
| 洛氏硬度 |
Scale M |
ASTM D-785 |
63 |
--- |
| 冲击下机械性能 |
--- |
UL 746B |
210 |
ºC |
| 拉伸强度 |
23℃,1.6mm |
ASTM D-638 |
173 |
MPa |
| 拉伸强度 |
23℃,3.2mm |
ASTM D-638 |
150 |
MPa |
| 断裂伸长率 |
23℃,1.6mm |
ASTM D-638 |
1.6 |
% |
| 断裂伸长率 |
23℃,3.2mm |
ASTM D-638 |
1.7 |
% |
| 拉伸模量 |
23℃,1.6mm |
ASTM D-638 |
19306 |
MPa |
| 拉伸模量 |
23℃,3.2mm |
ASTM D-638 |
18000 |
MPa |
| 弯曲模量 |
23℃,0.8mm |
ASTM D-790 |
18000 |
MPa |
| 弯曲模量 |
23℃,1.6mm |
ASTM D-790 |
14000 |
MPa |
| 弯曲模量 |
23℃,3.2mm |
ASTM D-790 |
13100 |
MPa |
| 无缺口冲击强度 |
23℃,1.6mm |
ASTM D-4812 |
840 |
j/m |
| 无缺口冲击强度 |
23℃,3.2mm |
ASTM D-4812 |
555,20%NB |
j/m |
| 弯曲强度 |
23℃,0.8mm |
ASTM D-790 |
215 |
MPa |
| 弯曲强度 |
23℃,1.6mm |
ASTM D-790 |
192 |
MPa |
| 弯曲强度 |
23℃,3.2mm |
ASTM D-790 |
183 |
MPa |
| 压缩强度 |
3.2mm |
ASTM D-695 |
89 |
MPa |
| 弯曲疲劳 |
3.2mm，69MPa |
ASTM D-671 |
2667 |
cycle |
| IZOD冲击强度 |
23℃,0.8mm |
ASTM D-256 |
400,40%NB |
j/m |
| IZOD冲击强度 |
23℃,1.6mm |
ASTM D-256 |
170 |
j/m |
| IZOD冲击强度 |
23℃,3.2mm |
ASTM D-256 |
225 |
j/m |
| 电气性能 |
介电强度 |
1.6mm逐步 |
ASTM D-149 |
31 |
KV/mm |
| 介电强度 |
23℃,1.6mm短时间 |
ASTM D-149 |
35 |
KV/mm |
| 介电强度 |
23℃,3.2mm短时间 |
ASTM D-149 |
＞28 |
KV/mm |
| 表面电阻率 |
--- |
ASTM D-257 |
1×1015 |
Ω |
| 体积电阻率 |
--- |
ASTM D-257 |
1×1016 |
Ω.cm |
| 损耗因素 |
23℃,3.2mm,1×109Hz |
ASTM D-2520B |
0.004 |
--- |
| 损耗因素 |
23℃,0.8mm,1×109Hz |
ASTM D-2520B |
0.004 |
--- |
| 损耗因素 |
23℃,1.6mm,1×109Hz |
ASTM D-2520B |
0.004 |
--- |
| 损耗因素 |
23℃,0.8mm,1×103Hz |
ASTM D-150 |
0.013 |
--- |
| 损耗因素 |
23℃,3.2mm,1×103Hz |
ASTM D-150 |
0.013 |
--- |
| 损耗因素 |
23℃,0.8mm,1×106Hz |
ASTM D-150 |
0.029 |
--- |
| 损耗因素 |
23℃,3.2mm,1×106Hz |
ASTM D-150 |
0.029 |
--- |
| 介电常数 |
23℃,0.8mm,1×103Hz |
ASTM D-150 |
3.9 |
--- |
| 介电常数 |
23℃,3.2mm,1×103Hz |
ASTM D-150 |
4.3 |
--- |
| 介电常数 |
23℃,0.8mm,1×106Hz |
ASTM D-150 |
3.5 |
--- |
| 介电常数 |
23℃,3.2mm,1×106Hz |
ASTM D-150 |
3.8 |
--- |
| 介电常数 |
23℃,0.8mm,1×109Hz |
ASTM D-2520B |
4.4 |
--- |
| 介电常数 |
23℃,3.2mm,1×109Hz |
ASTM D-2520B |
4.3 |
--- |
| 加工性能 |
熔解温度范围 |
℃ |
--- |
363～371 |
--- |
| 模具温度范围 |
℃ |
--- |
30～95 |
--- |
| 干燥时间（除湿干燥剂） |
--- |
--- |
2 |
h |
| 干燥温度 |
--- |
--- |
135 |
℃ |
| 加工时水气含量 |
--- |
--- |
＜0.01 |
% |
| 热 性 能 |
相关温度指数 |
--- |
UL 746B |
240 |
ºC |
| 熔点 |
--- |
ASTM D-3418 |
352 |
ºC |
| 导热性 |
--- |
ASTM C-177 |
0.32 |
W/m k |
| 热变形温度 |
--- |
ASTM D-648 |
289 |
ºC |
| 玻璃转变温度 |
--- |
ASTM D-3418 |
120 |
ºC |
| 外推最终融温 |
--- |
ASTM D-3418 |
360 |
ºC |
| 其它性能 |
厚度测试 |
--- |
UL 94 |
0.75 |
mm |
| 限制氧气指数 |
3.2mm |
ASTM D-2863 |
39 |
% |
| 厚度比率 |
--- |
UL 94 |
V-0 |
--- |
| |