HB-YD114(Q) |
1.6 |
50-55 (受强烈冲击后 After high impact) |
高锰钢堆焊焊丝，受强烈冲击后，表面具有加工硬度的特点。 High-manganese steelhardfacing flux-cored wires, and applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening. |
|
HB-YD115(Q) |
1.6 |
50-55 (受强烈冲击后After high impact) |
用于受严重冲击高锰钢堆焊，加工硬化效果显著。 Applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening. |
|
HB-YD165(Q) |
1.6 |
60-65 |
高硬度耐磨焊丝，适用于磨粒磨损表面堆焊 High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding. |
|
HB-YD172(Q) |
1.6 |
≥40 |
用于堆焊齿轮、挖泥斗、矿山机械等磨损件 Applied to repair surface of high impact wear parts, such as gear aud bucket and mining machinery. |
|
HB-YD207(Q) |
1.6 |
≥50 |
用于堆焊推土机 ，螺旋桨等磨损零件 Applied to repair surface of high wear parts, such as bulldozer blade and propeller. |
|
HB-YD212(Q) |
1.2/1.6 |
≥50 |
用于堆焊各种受磨损的机件表面，如齿轮、挖斗、矿山机械 Applied to repair surface of wear parts, such as gear mud bucket and mining machinery. |
|
HB-YD256(Q) |
1.6 |
HB≥170 |
高锰钢堆焊，适用于破碎机等受冲击磨损部位的堆焊 High-manganese steelhardfacing flux-cored Wires,it is applied to repair surface of high impact wear parts, such as Crusher. |
|
HB-YD258(Q) |
1.6 |
55-60 |
用于耐磨表面堆焊 Applied to repair surface of wear parts. |
|
HB-YD265(Q) |
1.6 |
60-65 |
高硬度耐磨焊丝，适用于磨粒磨损表面堆焊 High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding. |
|
HB-YD322(Q) |
1.6 |
≥55 |
用于堆焊各种冲模及切削刃具，兼用于修复要求耐磨损性能较高之机械零件 Applied to repair surface ofhigh wear resistanceparts, such as die and cuttingcutlery. |
|
HB-YD327A(Q) |
1.6 |
≥55 |
专门用于模具堆焊，耐磨性能高于D322 Used tomouldsurfacing, wear resistance is better than D322. |
|
HB-YD337(Q) |
1.6 |
≥48 |
用于铸钢或锻钢上堆焊锻模 Applied to repairforging dieatcast steelorforging steel. |
|
HB-YD397(Q) |
1.6 |
≥40 |
用于堆焊铸钢或锻钢做坯体的热锻模或堆焊高强度耐磨件 Applied to repair hotforging dieatcast steelor forging steel, or highstrengthwear surfacing. |
|
HB-YD40 (Q) |
1.6 |
50-59 |
用于热轧辊开坯辊堆焊 Applied to repair hot-rolling blooming rollor. |
|
HB-YD430A(Q) |
1.6 |
20-35 |
打底层堆焊焊丝 A backing hardfacing flux-cored Wires |
|
HB-YD488A(Q) |
1.6 |
45-50 |
用于轧辊堆焊 Applied to repair rollor |
|
HB-YD507Mo(Q) |
1.6 |
35-45 |
用于510℃以下中高压阀门堆焊 Applied to valve which operating tdivperature is less than 510℃. |
|
HB-YD518(Q) |
1.6 |
40-50 |
用于连铸辊堆焊 Applied to repaircontinuous caster roller |
|
HB-YD688(Q) |
1.6 |
50-60 |
用于磨煤辊打底焊(韧性好，可以多层堆焊) Used to coal roller backing welding. |
|
HB-YD788(Q) |
1.6 |
55-62 |
硬度高，可以多层堆焊。 High hardness andmulti-layer welding |
|
HB-YD888(Q) |
1.2, 1.6 |
60-65 |
硬度高，堆焊层厚度不超过6mm。 High hardness, but thethicknessofsurfacing layeris less than 6mm. |
|
HB-YD888Ni(Q) |
1.2 |
58-65 |
高铬合金焊丝，用于耐磨表面堆焊 Applied to repair surface of wear parts. |
|
HB-YD988(Q) |
1.6 |
55-63 |
高铬合金焊丝，用于耐磨表面堆焊 Applied to repair surface of wear parts. |
|
HB-YD990(Q) |
1.6 |
55-65 |
用于高温耐磨堆焊。 Applied to repair surface ofhigh tdivperaturewear parts. |
|
HB-YD58(Q) |
1.6 |
55-60 |
高温耐磨焊丝，用于化推焦机磨靴的堆焊。 high tdivperaturewear hardfacing wires, |
|
HB-YD67(Q) |
1.6 |
58-63 |
用于耐磨表面堆焊 Applied to repair surface of wear parts. |
|
HB-YD95(Q) |
1.6 |
55-63 |
高铬合金焊丝，用于耐磨表面堆焊 Applied to repair surface of wear parts. |
|
HB-DG7(Q) |
1.6 |
52-60 |
地铁盾构施工 刃口堆焊专用，也可用于煤碳石装载机料斗和刃口堆焊修复。 Applied to repair surface of high impact wear parts, such as shiled machine, exc ator bucket and hopper of mining machinery products. |