| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 比重 | ASTM D-792 | 1.41 | |||
| 吸收率 | 23℃,60%RH | ASTM D-570 | 0.22 | % | ||
| 机械性能 | 表面电阻率 | ASTM D-257 | 1×1016 | Ω | ||
| 伸缩率 | 23℃ | ASTM D-638 | 55 | % | ||
| 120D冲击强度 | Notch t3.2mm | ASTM D-256 | 6.0 | kgf.cm/cm | ||
| 拉伸冲击强度 | t3.2mm S type | ASTM D-1822 | 105 | kgf.cm/cm2 | ||
| 断裂强度 | t2mm | ASTM D-732 | 560 | kgf.cm/cm2 | ||
| 洛氏硬度 | ASTM D-785 | M80 | M scale | |||
| 曲折弹性率 | 23℃ | ASTM D-790 | 2.50 | ×104kgf/cm2 | ||
| 拉伸强度 | 23℃ | ASTM D-638 | 580 | kgf.cm/cm2 | ||
| 弯曲强度 | 23℃ | ASTM D-790 | 820 | kgf.cm/cm2 | ||
| 电气性能 | 耐电压 | ASTM D-149 | 19 | KV/mm | ||
| 导电率 | 106HZ | ASTM D-150 | 3.7 | |||
| 个质损耗系数 | 106HZ | ASTM D-150 | 0.007 | |||
| 体积电阻率 | ASTM D-257 | 1×1014 | Ω.cm | |||
| 热性能 | 燃烧性 | t0.8mm | UL 94 | HB | ||
| 线膨胀系数 | 20℃-80℃ | ASTM D-696 | 13 | ×10-5cm/cm/℃ | ||
| 熔体流动速率 | ASTM D-1238 | 10 | g/10min | |||
| 热变形温度 | 4.6kgf/cm2 | ASTM D-256 | 158 | ℃ | ||
| 18.6kgf/cm2 | ASTM D-256 | 110 | ℃ | |||
| 熔点 | 10℃/min | DSC Method | 165 | ℃ | ||
| 其它性能 | 成型收缩率 | t3mm,直径100mm | 2.0 | % | ||